Technical Sheet for ASI 505

Type .................................................................................. One-part, self-leveling RTV

Appearance ..........................................................................Smooth thick liquid

Specific Gravity .....................................................................Clear 1.02; Colors 1.04

Application Temperature Range ..................................................-18°C to +5O°C (0°F to +120°F)

Cure Method ..........................................................................Acetoxy, moisture cure

Skin Over Time........................................................................15 minutes

Cure Time .............................................................................24 hours (1/8" thickness)

Slump/Sag .............................................................................Flowable

Viscosity ...............................................................................Approx. 45,OOOcP

at 25°C (77°F) and 50% R.H. for 7 days (1/8" thickness)

Durometer Hardness (Shore A) (ASTM D 2240) ..................................30

Tensile Strength (ASTM D 412) .....................................................220 psi (1.5 MPa)

Elongation at Break (ASM D 412) ...................................................225%

Tear Resistance (ASTM D 624, Die B) ..............................................18 ppi (3.2 kN/m)

Temperature Range After Cure .....................................................-57°C to +204°C (-70°F to +400°F)

Shrink Factor ..........................................................................Nil

Thermal Expansion Coefficient .....................................................9 x 10⁴ 1/K

        0° to 100°C (32°F to 212°F)

Dielectric Strength (ASTM D 149) ..................................................500 volts/mil (215 kV/cm)

Volume Resistivity (ASTM 0 257) ...................................................1 x 10¹⁵ ohm/cm

Dissipation Factor (ASTM D 150)....................................................002at100Hz

                                                                                                                   0.002 at 10 kHz

Dielectric Constant (ASTM D 150) ..................................................60 at 100 kHz

                                                                                                                  2.60 at 10 kHz